A super high build, glass flake pure epoxy coating, which provides excellent resistance to water, chemicals and abrasion and good cathodic protection.本页参数：体积固体份 80 ± 2%、干膜厚度 200-500 μm、理论涂布率 1.60 m²/L。
以上内容整理自原厂说明书与本站参数表；选型、配套与货期请联系我们确认。
| 体积固体份 | 80 ± 2% |
|---|---|
| 干膜厚度 | 200-500 μm |
| 理论涂布率 | 1.60 m²/L (500 μm) |
| VOC | 162 g / L as supplied |
| 密度/比重 | — |
| 组份数 | — |
| 稀释剂 | NIPPON MARINE THINNER / NIPPON MARI… |
| 混合比 | BASE 79.5 / HARDENER 20.5 |
| 颜色/外观 | Gray ,Red oxide |
本型号原厂说明书未标注涂层位置与树脂类型，暂未归入上述分类；可按分类浏览同类产品，或联系我们确认配套体系。
A super high build, glass flake pure epoxy coating, which provides excellent resistance to water, chemicals and abrasion and good cathodic protection.
Anticorrosive for rudders, stern frames, sea chest, boottop, keel plate, etc. where significant damage is expected from abrasion and corrosion.
| Type | Epoxy (High build / Glass flake / Two-pack) |
|---|---|
| Color | Gray ,Red oxide |
| Gloss | Flat |
| Volume Solids | 80 ± 2% (ISO3233:1998) |
| Typical Dry Film Thickness | 200 ~ 500 μm |
| Approx. Wet Film Thickness | 250 ~ 625 μm |
| Theoretical Coverage | 1.60 m²/ L (500 μm) |
| Drying Time | Surface Dry | 6 hours (5℃) | 2 hours (20℃) | 1 hours (30℃) |
| Dry Hard | 24 hours (5℃) | 8 hours (20℃) | 6 hours (30℃) | |
| Full Cure | 14 days (5℃) | 7 days (20℃) | 5 days (30℃) | |
| Interval before Overcoating | Min. | 24 hours (5℃) | 8 hours (20℃) | 6 hours (30℃) |
| ( by self ) | Max. | 14 days (5℃) | 7 days (20℃) | 5 days (30℃) |
| VOC Values | 162 g / L as supplied |
|---|---|
| Thinner | NIPPON MARINE THINNER / NIPPON MARINE THINNER 615 (China Regions) |
Airless Spray
| Tip range | 0.89 ~ 0.99 mm |
|---|---|
| Fan angle | 55° ~ 62° |
| ( For T/U ) | 30° Output pressure above 225 kg / cm² |
| Mixing Ratio by Volume | BASE 79.5 / HARDENER 20.5 |
| Pot Life after Mixing | 4 hours (5℃) |
| 1.5 hours (20℃) | 45 min (30℃) |
| Packaging | Two Packs |
| Japan Local Brand | NIPPON E-MARINE 1000GF |
| Flash Point | BASE 28 ℃, HARDENER 31.5 ℃ |
Blast cleaned to ISO-Sa 2 1/2 or power tool cleaned to ISO-St 3 is recommended.
Please consult with Nippon Paint Marine representatives for water
Take precautions to avoid skin and eye contact (i.e. gloves, concentrations within safe limits.
Prior to use, obtain, consult and follow the SDS for this product concerning health and safety information.
1)The information contained in this sheet is liable to modification from time to time in the light of experience and our policy of continuous product development.
2)Use high ratio types of airless spray equipment (ex. Asahi Sunac Mammoth above 45 : 1). The viscosity increases at low temperatures, particularly during winter and the paint cannot be applied with the airless spray of normal types. The high ratio types prevent from sagging caused by excessive dilution with thinner.
3)To prevent spray gun from clogging, remove all filters in the spray guns and surge chambers.
Ball tip is recommended.
4) At temperatures below 10℃, it will take longer to dry and harden.
5)Avoid mixing a large amount of paint at one time because the usable time is shorter during high temperatures such as summer (30℃: 45 minutes).
6) For availability of product consult Nippon Paint Marine representatives.
7) Unit size and filled volumes can vary due to local regulations.
8) Use products that comply with local regulations to clean the paint equipment.
9) Store the paints in paint store.
资料以厂商最新版为准，具体以原厂最新 TDS 为准。查看 立邦船舶 NIPPON MARINE NIPPON E-MARINE 1000 GF 原厂 PDF 说明书全文。
原厂包装规格与批次交期以实际供货为准，可联系我们按项目核算。