THERMOTECT WR 耐热漆WR 属耐高温漆。用于有保温和无保温的高温钢结构。Under Insulation). 无机共聚物耐热涂料，用于CUI(防护层下防腐)。本页参数：体积固体份 54 ± 2%、组份数 双组份。同品牌同类可对比：THERISO UNDERCOAT、THERMOTECT EP 环氧耐热漆EP。
以上内容整理自原厂说明书与本站参数表；选型、配套与货期请联系我们确认。
| 体积固体份 | 54 ± 2% |
|---|---|
| 干膜厚度 | 100-150 微米/道 |
| 理论涂布率 | — |
| VOC | 396g/L |
| 密度/比重 | — |
| 组份数 | 双组份 |
| 闪点 | 25℃ |
| 稀释剂 | 专用稀释剂X |
| 混合比 | Base/Hardener=19/1(by weight) |
| THERMOTECT WR | 耐热漆WR |
|---|
A heat resistance paint based on inorganic copolymer for preventing CUI(Corrosive
Under Insulation).
无机共聚物耐热涂料,用于CUI(防护层下防腐)。
An insulated and non insulated steel structure for high temperature services
用于有保温和无保温的高温钢结构
Suitable for high temperature(up to 650℃)
用于高温部位(达到650℃)
Suitable for insulated and non insulated surface
用于保温和非保温的表面
Cyclic services in temperature between -185℃-540℃
可在-185℃-540℃之间提供良好保护性能
Good applicability
良好的施工性
Good weather resistance
良好的耐候性
| Color | Grey with aluminium effect |
|---|---|
| 颜色 | 铝灰色 |
| Volume Solids 体积固体份 | 54±2% |
| VOC | 396g/L, |
| 挥发性有机化合物含量 | 396g/L |
| Flash Point | 25℃ |
| 闪点 | Dry :100-150 microns/coat Wet : 185-278microns/coat |
| Film thickness | 干膜:100-150 微米/道湿膜:185-278 微米/道 |
| 涂装膜厚 | 0.344Kg/m2/125 microns |
0.344 千克/平方米/125 微米
| Theoretical Coverage | Practical coverage depending on surface conditions, environment, applications, etc. |
|---|---|
| 理论涂布率 | 实际涂布率与表面处理, 外界环境, 施工方法等多种因素有关。 |
| Temperature resistance | Non-continuous: 650℃Continuous: 540℃ |
| 耐热温度 | 非连续耐温:650℃,连续耐温:540℃ |
| Application Temperature 施工温度 | 5℃-40℃ |
|---|---|
| Mixing | Combine Base with Hardener, mix thoroughly with power agitator |
| 混合 | 混合主剂与固化剂,使用动力工具搅拌均匀 |
| Mixing Ratio | Base/Hardener=19/1(by weight) |
| 混合比例 | 主剂/固化剂=19/1(重量比) |
| Pot Life | 10℃ | 20℃ | 30℃ |
| 混合使用期 | 14hrs | 12hrs | 8hrs |
| Application Methods | Airless spray, air spray, brush and roller |
|---|---|
| 施工方法 | 无气喷涂、空气喷涂、刷涂、滚涂 Airless spray 无气喷涂 |
| Nozzle tip | 喷嘴尺寸 | No. 163-415~621 |
| Nozzle pressure | 出口压力 | ≥10Mpa |
| Thinning ratio | 稀释比率 | 0-5% by weight(重量比) |
Brush and roller
Thinning ratio 稀释比率 0-5% by weight(重量比)
| Thinner | Paint Thinner X |
|---|---|
| 稀释剂 | 专用稀释剂X |
| Drying time & | Temperature | 温度 | 10℃ | 20℃ | 30℃ |
| Overcoating interval | Surface dry | 指触干燥 | 3hrs | 2hrs | |
| 干燥时间&涂装间隔 | Touch dry | 半硬干燥 | 16hrs | 6hrs | |
| Min. interval | 最小涂装间隔 | 24hrs | 6hrs | ||
| Max. interval | 最大涂装间隔 | 7days | |||
Drying time may vary depending on film thickness,ventilation,humidity,undercoat paint condition etc.
干燥时间与涂装厚度,通风条件,相对湿度,下涂层的干燥情况有关。
| Applied Substrate | Bare steel |
|---|---|
| 适用底材 | 裸钢 |
| Typical topcoat | THERMOTECT WR or according to the coating system of Cosco Kansai. |
| 适用上涂 | THERMOTECT WR 或参考我司涂装配套 |
Store in dry, cool condition and away from sources of heat and ignition. Containers
must be kept tightly closed. Store condition shall be in accordance with national regulations
贮存于干燥阴凉的环境中,远离热源及火源。包装桶必须保持封闭。储存条件 遵循国家法规。
| Shelf life | Base:12 months ,Hardener: 6 months from date of production (25℃) |
|---|---|
| 贮存期限 | 自生产之日起,主剂12 个月,固化剂6 个月(25℃) |
The information given on this sheet is to the best of our knowledge and accurate at
the time of issuing. Since conditions of use are beyond the manufacturer’s control, information contained herein is without warranty, implied or otherwise, and the suitability of the material for the use contemplated is the sole responsibility of the buyer. The information contained on this data sheet is subject to modification at any time due to our policy of modification and product development.Please check this date sheet is current prior to using the product.
本说明书所提供信息均为目前我方所掌握最全面正确的资料,鉴于产品使用条件 非我方所能控制,此中信息不含担保,即仅在选取产品上对买方负责。由于我 公司产品及生产工艺的不断发展,本说明书的内容也会随时进行更改,此中所 有信息均以我方确认为主。产品使用前,请确认所持说明书为最新版本。
| Issued Date 发行日期 | 2024/07 |
|---|
资料以厂商最新版为准，具体以原厂最新 TDS 为准。查看 关西 KANSAI THERMOTECT WR 耐热漆WR 原厂 PDF 说明书全文。
原厂包装规格与批次交期以实际供货为准，可联系我们按项目核算。