SD ZINC 1000HA 无机硅酸锌车间底漆1000HA 属富锌底漆，无机硅酸锌漆体系。推荐用于车间底漆自动喷涂系统。以改性硅酸乙酯和锌粉为基料的车间底漆。本页参数：体积固体份 28 ± 2%、干膜厚度 15-25 微米/道、理论涂布率 18.7 平方米/升。同品牌同类可对比：SILISAFE ZINC SW-30 水性无机硅酸锌车间底漆SW-30、SILISAFE ZINC 80 水性无机富锌底漆80、AMEINCOAT ZINC PRIMER。
以上内容整理自原厂说明书与本站参数表；选型、配套与货期请联系我们确认。
| 体积固体份 | 28 ± 2% |
|---|---|
| 干膜厚度 | 15-25 微米/道 |
| 理论涂布率 | 18.7 平方米/升 /15 微米 |
| VOC | — |
| 密度/比重 | — |
| 组份数 | 双组份 |
| 闪点 | 14℃以上 |
| 稀释剂 | 专用稀释剂 |
| 混合比 | Base/Hardener=55/45(by weight) |
| SD ZINC PRIMER 1000HA(S) | 无机硅酸锌车间底漆1000HA(S) |
|---|
A shop primer based on modified ethyl silicate and zinc powder
以改性硅酸乙酯和锌粉为基料的车间底漆
Recommended for use with automatic shop priming systems
推荐用于车间底漆自动喷涂系统
Excellent high speed welding performance
优良的高速焊接性能
Outstanding gas cutting properties
极好的气割性能
Can be overcoated with a wide range of topcoat systems
能与多种上层涂料配套
Excellent corrosion resistance in the long term
优良的长期防腐性能
Excellent resistance to abrasion, heat and bending
极好的耐磨损、耐热、耐屈曲性能
| Color | Grey, and Oxide Red |
|---|---|
| 颜色 | 灰色和铁红色 |
| Volume Solids 体积固体份 | 28±2% |
| Flash Point | Greater than 14℃ |
| 闪点 | 14℃以上 |
| Film thickness | Dry : 15-25 microns/coat Wet : 54-89microns/coat |
| 涂装膜厚 | 干膜: 15-25 微米/道湿膜:54-89 微米/道 |
| Theoretical Coverage | 18.7 m2/L/15microns |
| 理论涂布率 | 18.7 平方米/升/15 微米 |
Practical coverage depending on surface conditions, environment, applications, etc.
实际涂布率与表面处理, 外界环境, 施工方法等多种因素有关。
| Application Temperature 施工温度 | 5℃-40℃ |
|---|---|
| Mixing | Add and mix thinner to base first, then add liquid to mix |
| 混合 | 先将主剂与稀释剂混合,再加入液 |
| Mixing Ratio | Base/Hardener=55/45(by weight) |
| 混合比例 | 主剂/固化剂=55/45(重量比) |
| Pot Life | 5℃ | 10℃ | 20℃ | 30℃ |
| 混合使用期 | 24hrs | |||
| Application Methods | Airless spray, air spray, brush and roller |
|---|---|
| 施工方法 | 无气喷涂、空气喷涂、刷涂、滚涂 Airless spray 无气喷涂 |
| Nozzle tip | 喷嘴尺寸 | 0.43mm-0.53mm |
| Nozzle pressure | 出口压力 | ≥10Mpa |
| Thinning ratio | 稀释比率 | 0-10% by weight(重量比) |
Brush/Roller 刷涂、滚涂 Thinning ratio 稀释比率 0-10% by weight(重量比)
| Thinner | SD Zinc 1000HA(S) Thinner |
|---|---|
| 稀释剂 | 专用稀释剂 |
| Drying time & | Temperature | 温度 | 5℃ | 20℃ | 30℃ |
| Overcoating interval | Surface dry | 指触干燥 | 3mins | 1.5mins | 1min |
| 干燥时间&涂装间隔 | Touch dry | 半硬干燥 | 5mins | 3mins | 2mins |
| Min. interval | 最小涂装间隔 | 24hrs | |||
| Max. interval | 最大涂装间隔 | ||||
| Applied Substrate | Bare steel |
|---|---|
| 适用底材 | 裸钢 |
| Typical topcoat | Various of primers |
| 适用上涂 | 多种底漆 |
Store in dry, cool condition and away from sources of heat and ignition. Containers must be kept
tightly closed.
贮存于干燥阴凉的环境中,远离热源及火源。包装桶必须保持封闭。
| Shelf life | 6 months from date of production (25℃) |
|---|---|
| 贮存期限 | 自生产之日起6 个月(25℃) |
The information given on this sheet is to the best of our knowledge and accurate at the time of
issuing. Since conditions of use are beyond the manufacturer’s control, information contained herein is without warranty, implied or otherwise, and the suitability of the material for the use contemplated is the sole responsibility of the buyer. The information contained on this data sheet is subject to modification at any time due to our policy of modification and product development.Please check this date sheet is current prior to using the product.
本说明书所提供信息均为目前我方所掌握最全面正确的资料,鉴于产品使用条件非我方所 能控制,此中信息不含担保,即仅在选取产品上对买方负责。由于我公司产品及生产工艺 的不断发展,本说明书的内容也会随时进行更改,此中所有信息均以我方确认为主。产品 使用前,请确认所持说明书为最新版本。
| Issued Date 发行日期 | 2024/05 |
|---|
资料以厂商最新版为准，具体以原厂最新 TDS 为准。查看 关西 KANSAI SD ZINC 1000HA(S) 无机硅酸锌车间底漆1000HA(S) 原厂 PDF 说明书全文。